The formation and hydrogen sorption properties of the NaMgH3 perovskite/type hydride have been examined. Samples were mechanically ball milled under argon for 2, 5 and 15 h; then characterized by X-ray diffraction (XRD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA) coupled with a mass spectrometer (MS). Lattice parameters and cell volume of the main NaMgH3 phase increase as a function of milling. Dehydrogenation proceeded in two-step reactions for the NaMgH3 . The maximum amount of released hydrogen was achieved for the 2 h milled NaMgH3 hydride accounting for 5.8 wt.% of H2 from 287 ?C to 408 ?C. Decomposed NaMgH3 samples were reversibly hydrogenated under 10 bar H2 at ~200 ?C
Las propiedades de formación y sorción de hidrógeno de la perovskita/tipo hidruro de NaMgH3han sido examinados. Las muestras se molieron mecánicamente con bolas bajo argón durante 2, 5 y 15 h; luegocaracterizado por difracción de rayos X (XRD), calorimetría diferencial de barrido (DSC) y análisis termogravimétrico (TGA) junto con un espectrómetro de masas (MS). Parámetros de red y volumen de celda deel aumento de la fase principal de NaMgH3 en función de la molienda. La deshidrogenación se realizó en dos pasos.reacciones para el NaMgH3. La cantidad máxima de hidrógeno liberado se logró durante las 2 hhidruro de NaMgH3 molido que representa el 5,8% en peso de H2de 287 ?C a 408 ?C. NaMgH3 descompuestolas muestras se hidrogenaron reversiblemente bajo 10 bar H2 a ~200 ?C